Facile Synthesis of Si@SiC Composite as an Anode Material for Lithium-Ion Batteries

Here, we propose a simple method for direct synthesis of a Si@SiC composite derived from a SiO 2 @C precursor via a Mg thermal reduction method as an anode material for Li-ion batteries. Owing to the extremely high exothermic reaction between SiO 2 and Mg, along with the presence of carbon, SiC can be spontaneously produced with the formation of Si. The synthesized Si@SiC was composed of well-mixed SiC and Si nanocrystallites. The SiC content of the Si@SiC was adjusted by tuning the carbon content of the precursor. Among the resultant Si@SiC materials, the [email protected] sample, which was produced from a precursor containing 4.37 wt % of carbon, exhibits excellent electrochemical characteristics, such as a high first discharge capacity of 1642 mAh g –1 and 53.9% capacity retention following 200 cycles at a rate of 0.1C. Even at a high rate of 10C, a high reversible capacity of 454 mAh g –1 was obtained. Surprisingly, at a fixed discharge rate of C/20, the [email protected] electrode delivered a high capacity of 989 mAh g –1 at a charge rate of 20C. In addition, a full cell fabricated by coupling a lithiated [email protected] anode and a LiCoO 2 cathode exhibits excellent cyclability over 50 cycles. This outstanding electrochemical performance of [email protected] is attributed to the SiC phase, which acts as a buffer layer that stabilizes the nanostructure of the Si active phase and enhances the electrical conductivity of the electrode.