A Rapid Process for Producing Cellulose Multi‐Filament Fibers from a NaOH/Thiourea Solvent System

Summary: Cellulose was dissolved rapidly in 9.5 wt.‐% NaOH and 4.5 wt.‐% thiourea aqueous solution pre‐cooled to −5 °C to prepare a transparent solution. Novel cellulose multi‐filament fibers were spun successfully, for the first time, from the cellulose dope on an extended laboratory scale. The results from 13C NMR, scanning electron microscopy and wide angle X‐ray diffraction (WAXD) patterns indicated that the fibers exhibited cellulose II character and possessed a circular cross‐section and smooth surface. The tensile strength of the novel fibers reached 1.9–2.2 cN · dtex−1. 2D WAXD and SAXS patterns revealed that, with a drawing progress, the orientation factor increased and mechanical properties were improved. SEM micrographs of the novel multi‐filament fibers spun from cellulose solution in a NaOH/thiourea aqueous system pre‐cooled to −5 °C on an extended laboratory scale. magnified image SEM micrographs of the novel multi‐filament fibers spun from cellulose solution in a NaOH/thiourea aqueous system pre‐cooled to −5 °C on an extended laboratory scale.