Synthesis of Pyrochlore‐Free 0.9Pb(Mg 1/3 Nb 2/3 )O 3 ‐0.1PbTiO 3 Ceramics via a Soft Mechanochemical Route

Single‐phase perovskite 0.9Pb(Mg 1/3 Nb 2/3 )O 3 ‐0.1PbTiO 3 (0.9PMN–0.1 PT) from a stoichiometric mixture of starting materials was synthesized by applying a mechanochemical technique to the stage of a precursor. A stoichiometric mixture of PbO, TiO 2 , Mg(OH) 2 , and Nb 2 O 5 was milled for 60 min and heated at temperatures as low as 850°C for 4 h to obtain a single phase. The maximum dielectric constant of the samples from the milled mixture increased as the sintering temperature increased, with the remarkable grain growth, and attained 24600 at 1200°C. In contrast, poor densification and coexistence of the pyrochlore phase were observed on the samples from the nonmilled mixture. Further observation suggested that the pyrochlore phase concentrated near the surface during sintering and then migrated into the PbZrO 3 packing powder, leading to a pyrochlore–free phase at 1250°C. The dielectric constant of the latter ceramics was explained by the series mixing rule for the dielectric constant of a diphasic solid.