Potential-Induced Degradation of CuIn₁₋ₓ GaₓSe₂ Thin Film Solar Cells

The use of Na-free or low Na content glass substrates is observed to enhance the resiliency to potential-induced degradation, as compared with glass substrates with high Na content, such as soda lime glass (SLG). The results from stress tests in this study suggest that degradation caused by a combination of heat and bias across the SLG substrate is linked to increased Na concentration in the CdS and Cu(In,Ga)Se2(CIGS) layers in CIGS-based solar cells. The degradation during the bias stress is dramatic. The efficiency drops to close to 0% after 50 h of stressing. On the other hand, cells on Na-free and low Na content substrates exhibited virtually no efficiency degradation. The degraded cells showed partial recovery by resting at room temperature without bias; thus, the degradation is nonpermanent and may be due to Na migration and accumulation rather than chemical reaction.