Preparation and characterization of surface‐modified ammonium polyphosphate and its effect on the flame retardancy of rigid polyurethane foam

A functional surface‐modification agent was synthesized via a reaction between hexachlorocyclotriphosphazene and γ‐aminopropyl triethoxysilane. Ammonium polyphosphate (APP) was modified with this agent and then incorporated into a rigid polyurethane foam (RPUF). Fourier transform infrared spectroscopy, 1H‐NMR, and X‐ray photoelectron spectroscopy were used to characterize the modified ammonium polyphosphate (M‐APP). The results show that the dispersibility was improved and the particle size decreased after the modification. The limiting oxygen index and cone calorimetry test results show that M‐APP enhanced the flame‐retardant properties of RPUF. The peak heat‐release rate of polyurethane (PU)/20% M‐APP decreased by 51.18% compared with that of PU–APP. The scanning electron microscopy results illustrate that M‐APP facilitated the formation of intumescent and compact char. The excellent flame‐retardant performance of M‐APP resulted from the flame‐inhibition and barrier effects, which were attributed to the phosphazene group and the intumescent char, respectively.