Structural and optical studies of nitrogen incorporation into GaSb-based GaInSb quantum wells

We investigate the incorporation of nitrogen into (Ga,In)Sb grown on GaSb and report room temperature photoluminescence from GaInSb(N) quantum wells. X-ray diffraction and channeling nuclear reaction analysis, together with Rutherford backscattering, were employed to identify the optimal molecular beam epitaxial growth conditions that minimized the incorporation of non-substitutional nitrogen into GaNSb. Consistent with this hypothesis, GaInSb(N) quantum wells grown under the conditions that minimized non-substitutional nitrogen exhibited room temperature photoluminescence, indicative of significantly improved radiative efficiency. Further development of this material system could enable type-I laser diodes emitting throughout the (3-5 μm) wavelength range.