Characteristics of metalorganic remote plasma chemical vapor deposited Al2O3 gate stacks on SiC metal–oxide–semiconductor devices

Metalorganic remote plasma chemical vapor deposited SiO2/Al2O3 stacks were deposited on 6H p-type silicon SiC to fabricate a high-k gate stack SiC metal–oxide–semiconductor capacitors. Capacitance–voltage (C–V) and current–voltage (I–V) measurements were performed. C–V characteristics showed excellent properties at room and higher temperatures. Samples exhibited a slight negative flatband shift from which the net oxide charge (Qox) was calculated. Low leakage currents were observed even at high temperatures. I–V characteristics of Al2O3 were superior to those observed on AlN and SiO2 dielectrics on SiC.