Long‐term study of high‐strength hydroxyapatite/poly(L‐lactide) composite rods for the internal fixation of bone fractures: A 2–4‐year follow‐up study in rabbits

Biodegradation of hydroxyapatite (HA)/poly(L-lactide)(PLLA) composite bone implant rods was studied with the use of two types of HA particles as reinforcing fillers: uncalcined HA (u-HA) or calcined HA (c-HA). Composite rods of u-HA/PLLA and c-HA/PLLA containing 30 or 40% (w/w) HA were implanted in the distal femur of 21 rabbits, and specimens were examined by light microscopy, scanning-electron microscopy (SEM), and transmission-electron microscopy (TEM) 2-4 years later. For u-HA/PLLA, trabecular bone bonding directly onto the rod was maintained for up to 2 years. By 3 years, surface collapse had begun, and the implants were shrinking. By 4 years, they had shrunk further, with complete bone encapsulation. The u-HA particles were small and needle shaped in the peripheries, and TEM confirmed their resorption. The cross-sectional area after 4 years decreased by 23.3+/-8.4%. The mean ratio of bony ingrowth to the initial cross-sectional area around the shrunken rods was 6.7+/-1.3 %. The viscosity molecular weight of PLLA reduced from 2 x 10(5) to less than 1 x 10(3). Thus, most of the PLLA had released from the rods. The c-HA/PLLA implants also showed good osteoconductivity, but shrinkage and infiltration of histiocytes were less. No osteolytic or osteoarthritic changes were found.