Direct and indirect electrocaloric measurements on 〈001〉-PbMg1/3Nb2/3O3-30PbTiO3 single crystals

A direct electrocaloric effect (ECE) measurement system, based on a modified-differential scanning calorimeter (DSC), allowing the acquisition of both thermal (ECE, heat capacity) and electrical (P-E loops, leakage current) information simultaneously, was used to analyze 〈001〉-oriented PbMg1/3Nb2/3O3-30PbTiO3 single crystals. Different electric-field-induced phase transitions were identified on direct ECE measurements and confirmed by dielectric measurements. The strongest ECE (ΔTEC = 0.65 K) was measured for an applied electric field E = 10 kV/cm just above the temperature of depolarization. The direct ECE measurements were compared with indirect measurements obtained from dielectric polarization measurements versus electric field and temperature and a very good agreement was found. A region with negative ΔTEC was identified by both direct and indirect measurements. This phenomenon was attributed to the formation of a reversible field-induced phase transition towards a state with a different polar direction.