Electrospinning of polystyrene/poly(2‐methoxy‐5‐(2′‐ethylhexyloxy)‐1,4‐phenylene vinylene) blends

Ultrafine polystyrene (PS)/poly(2‐methoxy‐5‐(2′‐ethylhexyloxy)‐1,4‐phenylene vinylene) (MEH‐PPV) fibers were successfully prepared by electrospinning of PS/MEH‐PPV solutions in chloroform, 1,2‐dichloroethane, and tetrahydrofuran (THF). Three concentrations of the solutions were prepared: 8.5, 16, and 23.5% (w/v), with the compositional weight ratios between PS and MEH‐PPV being 7.5:1, 15:1, and 22.5:1, respectively. Smooth fibers only observed from 23.5% (w/v) PS/MEH‐PPV solution in chloroform. Improvement in the electrospinnability of 8.5% (w/v) PS/MEH‐PPV solution in chloroform was achieved by addition of an organic salt, pyridinium formate (PF), or by addition of a minor solvent with a high dielectric constant value. The average diameters of the as‐spun PS/MEH‐PPV fibers were between 0.30 and 5.11 μm. Last, photoluminescence of 8.5% (w/v) solutions of PS/MEH‐PPV in a mixed solvent system of chloroform and 1,2‐dichloroethane of various volumetric compositions and the resulting as‐spun fibers was investigated and compared.