Phosphorus‐containing polyaryloxydiphenylsilanes with high flame retardance arising from a phosphorus–silicon synergistic effect

Polyaryloxydiphenylsilanes were prepared from phosphorus‐containing diols and diphenydichlorolsilane through solution polymerization. With a stoichiometric imbalance in feed monomers, the resulting polymers exhibited moderate melting points and good processing properties. The polymers prepared showed initial decomposition temperatures above 340 °C, excellent thermal stability, high char yields at 850 °C and very high limited oxygen index values of 56–59. The polymers' char yields and their (P + Si) contents showed linear relationships.