Effect of exfoliation and dispersion on the yield behavior of melt‐compounded polyethylene–montmorillonite nanocomposites

The yield behavior of melt‐mixed nanocomposites containing 5 wt % organically modified montmorillonite in matrices of a linear low‐density polyethylene (LLDPE) or a modified polyethylene was studied as a function of the temperature and strain rate. In the melt‐mixed LLDPE nanocomposite, the montmorillonite showed a slight increase in the clay spacing, which suggested that the clay was at best intercalated. Transmission electron microscopy (TEM) images showed that the dispersion in this nanocomposite was poor. The use of the modified polyethylene promoted exfoliation of the clay tactoids in the nanocomposite, as assessed by X‐ray diffraction and TEM. In both nanocomposites, the yield mechanisms were insensitive to the addition of the organoclay, even though modest increases in the modulus were produced.