This letter reports studies on highly strained and strain-compensated InGaAs quantum-well (QW) active diode lasers on GaAs substrates, fabricated by low-temperature (550/spl deg/C) metal-organic chemical vapor deposition (MOCVD) growth. Strain compensation of the (compressively strained) InGaAs QW is investigated by using either InGaP (tensile-strained) cladding layer or GaAsP (tensile-strained) barrier layers. High-performance /spl lambda/=1.165 μm laser emission is achieved from InGaAs-GaAsP strain-compensated QW laser structures, with threshold current densities of 65 A/cm2for 1500-μm-cavity devices and transparency current densities of 50 A/cm2. The use of GaAsP-barrier layers are also shown to significantly improve the internal quantum efficiency of the highly strained InGaAs-active laser structure. As a result, external differential quantum efficiencies of 56% are achieved for 500-μm-cavity length diode lasers.
No takes yet. Share an insight, caveat, or question.
Tansu et al. (2001) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: