A New Family of Nonstoichiometric Layered Rare-Earth Tin Antimonides, RESnxSb2 (RE = La, Ce, Pr, Nd, Sm): Crystal Structure of LaSn0.75Sb2

A new class of nonstoichiometric layered ternary rare-earth tin antimonides, RESn(x)()Sb(2) (RE = La, Ce, Pr, Nd, Sm), has been synthesized through reaction of the elements at 950 degrees C. In the lanthanum series LaSn(x)()Sb(2), tin can be incorporated from a maximum content of x approximately 0.7 or 0.8 to as low as x approximately 0.10. The structure of lanthanum tin diantimonide with the maximum tin content, LaSn(0.75)Sb(2), has been determined by single-crystal X-ray diffraction methods. It crystallizes in the orthorhombic space group -Cmcm with a = 4.2425(5) Å, b = 23.121(2) Å, c = 4.5053(6) Å, and Z = 4. The isostructural rare-earth analogues were characterized by powder X-ray diffraction. The structure of LaSn(0.75)Sb(2) comprises layers of composition "LaSb(2)" in which La atoms are coordinated by Sb atoms in a square-antiprismatic geometry. Between these layers reside chains of Sn atoms distributed over three crystallographically independent sites, each partially occupied at about 20%. The structure of LaSn(0.75)Sb(2) can be regarded as resulting from the excision of RE-Sb and Sb-Sb bonds in the related structures of binary rare-earth diantimonides, RESb(2), and then intercalation of Sn atoms between layers.