Significant Bauschinger effect and back stress strengthening in an ultrafine grained pure aluminum fabricated by severe plastic deformation process

Bauschinger test in uniaxial tension-compression mode was carried out for the first time on the pure Al specimens having homogeneous ultra-fine grained (UFG) microstructures fabricated by equal-channel angular pressing (ECAP) and subsequent annealing processes. Significant Bauschinger stress (transient softening), Bauschinger energy parameter and their strong dependences on the tensile plastic pre-strain at the very early stage of the tensile deformation were measured in the UFG specimens, in sharp contrast to their coarse-grained (CG) counterpart. The grain size dependence of the Bauschinger effect in pure Al was qualitatively discussed in terms of the back stress arising from the formation of dislocation pile-up against the grain boundary during plastic deformation.