Microstructure of hot-pressed α-Sic after creep experiments at high temperature

Transmission electron microscopy analyses of hot-pressed α-Sic deformed at 1600°C have shown the activation of the basal plane with glide dislocations dissociated into Shockley partials. Loop nucleations have been frequently observed along the dislocation lines and a climb mechanism is proposed to explain, the experimental analyses.