Synthesis and properties of new aromatic polyimides based on 2,5‐bis(4‐amino‐2‐trifluoromethylphenoxy)‐ tert ‐butylbenzene and various aromatic dianhydrides

A novel, fluorinated diamine monomer, 2,5‐bis(4‐amino‐2‐ trifluoromethylphenoxy)‐ tert ‐butylbenzene ( II ) was synthesized through the nucleophilic substitution reaction of tert ‐butylhydroquinone ( t ‐BHQ) and 2‐chloro‐5‐nitrobenzotrifluoride in the presence of potassium carbonate to yield the intermediate dinitro compound I , followed by catalytic reduction with hydrazine and Pd/C to afford diamine II . A series of fluorinated polyimides V were prepared from II with various aromatic dianhydrides ( III a–f ) via the thermal imidization of poly(amic acid). Most of V a–f could be soluble in amide‐type solvents and even in less polar solvents. These polyimide films showed tensile strengths up to 106 MPa, elongation at break up to 21%, and initial modulus up to 2.1 GPa. The glass‐transition temperature of V was recorded at 245–304 °C, the 10% weight loss temperatures were above 488 °C, and left more than 41% residue even at 800 °C in nitrogen. Low dielectric constants, low moisture absorptions, and higher and light‐colored transmittances were also observed.