Nature of Ptn/TiO2(110) Interface under Water-Gas Shift Reaction Conditions: A Constrained ab Initio Thermodynamics Study

The electronic structure of small Pt n ( n = 1–8) clusters supported on the stoichiometric and partially reduced rutile TiO 2 (110) surface have been investigated using density functional theory. Pt atoms prefer to form a close-packed structure with (111) facet near an oxygen vacancy of the TiO 2 support and a less dense structure with (100) facet away from oxygen vacant sites. The main focus of this study is on identifying a realistic catalyst model for the Pt/TiO 2 interface under water-gas shift (WGS) reaction conditions. Constrained ab initio thermodynamic simulations on the stability of oxygen vacancies and formation of adsorbed gas phase molecules such as oxygen, CO, and hydrogen at the metal/oxide interface reveal that under WGS reaction conditions the formation of surface oxygen vacancies are thermodynamically favorable, platinum oxide species (PtO x ) can easily be reduced and should not be present, CO adsorbs only weakly on interfacial Pt atoms, and CO poisoning of these sites should be less important. While hydrogen generally interacts weakly with interfacial Pt atoms, it forms very stable hydride species on Pt atoms neighboring an oxygen vacancy of the TiO 2 (110) support, possibly negatively affecting the WGS reaction rate.