Monoclinic and orthorhombic Fe(2)(MoO(4))(3) microsized particles with complex 3D architectures have been selectively prepared by a template-free hydrothermal process. The pH value, reaction time, temperature, and molybdenian source have crucial influence on the phase formation, shape evolution, and microstructures. Monoclinic Fe(2)(MoO(4))(3) particles obtained at pH 1 and pH 1.65 display ferromagnetic ordering at 10.4 K and 10.5 K, respectively, and the ferromagnetic component is determined to be 0.0458 mu(B) and 0.0349 mu(B) per Fe-ion at 10 K, respectively. For orthorhombic beta-Fe(2)(MoO(4))(3), antiferromagnetic ordering was observed about 12 K. At higher temperatures, beta-Fe(2)(MoO(4))(3) began to follow the Curie-Weiss law with theta=-70 K. Such 3D architectures of monoclinic and orthorhombic beta-Fe(2)(MoO(4))(3) microparticles with unique shapes and structural characteristics may find applications as catalysts and as well as in other fields.