The molar ratio of (Lu2O3/Lu2O3+ Gd2O3) and R1parameter of the LPE melt for (BiLuGd)3Fe5O12growth were varied to determine the region of pit-free thick film growth. The borderline between the presence and absence of pits is in the neighborhood of Gd2O3/Lu2O3= 1 in the melt. The magneto-optical properties of the 250 μm thick film were studied. 2408°/cm of the Faraday rotation (λ = 1.153 μm) and 37.4 dB of extinction ratio were obtained. This result confirms that it is suitable for compact isolators.