Synthesis of autophotosensitive hyperbranched polyimides based on 3,3′,4,4′‐benzophenonetetracarboxylic dianhydride and 1,3,5‐tris(4‐aminophenoxy)benzene via end capping of the terminal anhydride groups by ortho‐alkyl aniline

Benzophenone‐containing, anhydride‐terminated hyperbranched poly(amic acid)s were end‐capped by ortho‐alkyl aniline in situ and then chemically imidized, yielding autophotosensitive hyperbranched polyimides. The polyimides were soluble in strong polar solvents, such as N‐methyl‐2‐pyrrolidone, N‐dimethylformamide, dimethylacetamide, and dimethyl sulfoxide. Thermogravimetric analysis revealed their excellent thermal stability, with a 5 wt % thermal loss temperature in the range of 527–548 °C and a10 wt % thermal loss temperature in the range of 562–583 °C. The strong absorption of the polyimide films in ultraviolet–visible spectra at 365 nm indicated that the hyperbranched polyimides were patternable. Highly resolved images with a line width of 6 μm were developed by ultraviolet exposure of the polymer films. A well‐defined image with lines as thin as 3 μm was also patterned, but the lines were rounded at the edges.