Novel Polymer Clay‐Based Nanocomposites: Films with Remarkable Optical and Water Vapor Barrier Properties

The impact of varying the copolymer composition of styrene–co‐butyl acrylate copolymers on the dispersion of montmorillonite (MMT) clay and the effect thereof on the transparency and water vapor barrier properties of the resultant films is assessed. The hybrid latexes containing MMT clay concentrations of 10–30 wt% are prepared using miniemulsion polymerization. The morphology of the resultant latexes shows that the MMT particles are predominantly adhered onto the surface of the latex particles. However, the transparency of the films suggests a fair dispersion of the MMT platelets in the matrix. The thickness‐normalized light transmittance for copolymers with 40 and 50 mol% styrene only decreases from 70% in the neat films to 50% in the nanocomposite films containing 30 wt% clay. The best optical properties are observed for the copolymers with 30 mol% styrene, in which the light transmittance only decreases from 85% (unfilled film) to 60% in the nanocomposite films containing 30 wt% clay. Overall, the water vapor barrier properties are much higher in the copolymer films with 30 mol% styrene due to the unique morphological organization of MMT platelets in the matrix.