Si/SiGe Resonant Interband Tunneling Diodes Incorporating δ-Doping Layers Grown by Chemical Vapor Deposition

This is the first report of a Si/SiGe resonant interband tunneling diodes (RITDs) on silicon substrates grown by the chemical vapor deposition process. The nominal RITD structure forms two quantum wells created by sharp delta-doping planes which provide for a resonant tunneling condition through the intrinsic spacer. The vapor phase doping technique was used to achieve abrupt degenerate doping profiles at higher substrate temperatures than previous reports using low-temperature molecular beam epitaxy, and postgrowth annealing experiments are suggestive that fewer point defects are incorporated, as a result. The as-grown RITD samples without postgrowth thermal annealing show negative differential resistance with a recorded peak-to-valley current ratio up to 1.85 with a corresponding peak current density of 0.1 kA/cm2at room temperature.