Properties of Ag-Sheathed Bi-Pb-Sr-Ca-Cu-O Superconducting Tapes Prepared by the Intermediate Pressing Process

The influence of an intermediate pressing process on the superconducting properties of Ag-sheathed Bi-Pb-Sr-Ca-Cu-O superconducting tapes has been investigated. The critical current density (J c) was improved by the effect of the uniaxial pressing and by a sintering process after the initial sintering. The maximum transport J c at 77.3 K under zero magnetic field was indicated as 2.36×104 A/cm2, and that at 4.2 K under zero magnetic field was indicated as 1.5×105 A/cm2. The magnetic field dependence on the J c at 4.2 K was summarized as follows: 5×104 A/cm2 (I⊥H, C-axis⊥H, 10 T) and 3×104 A/cm2 (I⊥H, C-axis//H, 10 T).