A Kinetic Study on the Thermal Degradation of Multi‐Walled Carbon Nanotubes‐Reinforced Poly(propylene) Composites

Summary: The influence of the multi‐walled carbon nanotubes (MWNTs) content on the thermal degradation behavior of MWNTs‐reinforced poly(propylene) (PP) composites was investigated by using non‐isothermal thermogravimetric analysis (TGA). Kinetic parameters of degradation were evaluated by using the Flynn‐Wall‐Ozawa iso‐conversional method and the pseudo first‐order method. As a result, compared with pristine PP, MWNTs‐PP nanocomposites have lower peak temperatures of degradation, narrower degradation temperature ranges and a higher amount of residual weight at the end of the degradation, which is likely to be a result of specific interactions between complimentary functional groups. The values of the reaction order of MWNTs‐PP nanocomposites determined by the Kissinger method are close to 1 in the non‐isothermal degradation process. There is a good correlation between the Ea in region II and the peak temperature of degradation for the composites. Activation energies for degradation of different contents of MWNTs‐filled PP nanocomposites as a function of conversion. image Activation energies for degradation of different contents of MWNTs‐filled PP nanocomposites as a function of conversion.