Mode selection and high-quality upconversion lasing from perovskite CsPb2Br5 microplates

In recent years, halide perovskite nanostructures have had great advances and have opened up a bright future for micro/nanolasers. However, upconversion lasing by two-photon excitation with mode selection and high quality factor in one device is still rarely reported. Herein, two lasing modes are demonstrated in the all-inorganic perovskite CsPb 2 Br 5 microplates with subwavelength thickness and uniform square shape. The net optical gain is quickly established in less than 1 ps and persists more than 30 ps, revealed by ultrafast transient absorption spectroscopy. The temperature-dependent low-threshold amplified spontaneous emission confirms the net gain for stimulated emission with a high characteristic temperature of 403 K, far surpassing the all-inorganic CsPbBr 3 semiconductor gain media. Remarkably, upconversion lasing based on two kinds of microcavity effects, Fabry–Pérot and whispering-gallery modes, from the microplates at room temperature is successfully achieved with a low threshold operating in multi- or single-mode, respectively. Surprisingly, the quality factor ( ∼ 3551 ) is among the best values obtained from perovskite micro/nanoplate upconversion lasers without an external cavity. Moreover, the highly stable chromaticity with color drift only less than 0.1 nm also outbalances the all-inorganic CsPbBr 3 ones. These superior performances of CsPb 2 Br 5 microplate lasing with a facile solution synthesis procedure will offer a feasible structure to fabricate specific functionalities for high-performance frequency upconversion micro/nanoscale photonic integrated devices.