Femtosecond laser ablation properties of borosilicate glass

We study the femtosecond laser ablation properties of borosilicate glass using atomic force microscopy and laser pulses of 200 fs duration, centered at 780 nm wavelength. We show that both single-shot and multishot ablation threshold fluences can be determined by studying the diameter and the depth of single-shot ablated craters. The linear relationship between the square of the crater diameter and the logarithm of the laser fluence in the form of D2=2w02ln(F0∕FthN=1) provides the single-shot ablation threshold, FthN=1, whereas the linear relationship between the ablation depth and the logarithm of laser fluence in the form of ha=αeff−1ln(F0∕FthN>1) provides the multishot ablation threshold, FthN>1. The results depict a multishot ablation threshold of ≈1.7J∕cm2 independent of the atmospheric conditions. The slopes of the linear fits also provide a precise estimate of the beam radius at the surface, w0≈5.9μm, and the “effective optical penetration depth,” αeff−1≈238nm in air. The method is systematic, provides results that are consistent with the literature, and eliminates uncertainties because of instrument sensitivities. We also show that threshold measurement based on the extrapolation of volume to zero, a method used often in previous studies, is somewhat questionable. Finally, the measured dimensions of ablated craters reveal that the ablation volume per unit input energy is about 1.3–1.5μm3∕μJ at an intermediate fluence regime of 10