Tetragonal BaCoO 3 : A Co 4+ Ferromagnetic Mott Insulator

This is the authors' abstract. We don't add key points for this paper.

High Resolution Image Download MS PowerPoint Slide We report the stabilization of the metastable body-centered tetragonal (BCT) phase of BaCoO 3 (BCT-BaCoO 3 ) under high-pressure (15 GPa) and high-temperature (1200 °C) conditions using a mixture precursor. This double perovskite adopts the EuTiO 3 -type structure (space group I 4/ mcm ), as confirmed by powder X-ray diffraction and high-resolution STEM. X-ray photoelectron spectroscopy indicates a predominant Co 4+ oxidation state without detectable oxygen vacancies. Magnetization and heat capacity measurements reveal ferromagnetic ordering at T C ∼ 107 K, attributable to the BCT-BaCoO 3 phase. Above this temperature, the mixed-phase sample exhibits Curie–Weiss paramagnetism, a low-spin to high-spin crossover upon cooling, and a possible intermediate-spin state at elevated temperatures. Resistivity data indicates insulating behavior with weak magnetoresistance. DFT and DFT + DMFT calculations suggest that the insulating state originates from an orbitally selective transition sensitive to the nominal valence of the Co-d shell. The metastable BCT-BaCoO 3 phase cannot be retained in pure form at ambient pressure but can be stabilized by embedding it in a disordered mixture, offering a potential route to discover and preserve other high-pressure phases under ambient conditions.