Synthesis of poly(methyl methacrylate)‐b‐polystyrene containing a crown ether unit at the junction point via combination of atom transfer radical polymerization and nitroxide mediated radical polymerization routes

Poly(methyl methacrylate)‐b‐polystyrene (PMMA‐b‐PS) containing a benzo‐15‐crown‐5 unit at the junction point was prepared by combining atom transfer radical polymerization and nitroxide‐mediated radical polymerization. For this purpose, 6,7,9,10,12,13,15,16‐octahydro‐5,8,11,14,17‐pentaoxa‐benzocyclopentadecene‐2‐carboxylic acid 3‐(2‐bromo‐2‐methyl‐propionyloxy)‐2‐methyl‐2‐[2‐phenyl‐2‐(2,2,6,6‐tetramethyl‐piperidin‐1‐yloxy)‐ethoxycarbonyl]‐propyl ester (3) was synthesized and used as an initiator in atom transfer radical polymerization of methyl methacrylate in the presence of CuCl and pentamethyldiethylenetriamine at 60°C. A linear behavior was observed in both plots of ln([M]0/[M]) versus time and Mn,GPC versus conversion indicating that the polymerization proceeded in a controlled/living manner. Thus obtained PMMA precursor was used as a macroinitiator in nitroxide‐mediated radical polymerization of styrene (St) at 125°C to give well‐defined PMMA‐b‐PS with crown ether per chain. Kinetic data were also obtained for copolymerization. Moreover, potassium picrate (K+ picrate) complexation of 3 and PMMA‐b‐PS copolymer was studied.