Effect of Mg loading on the high-frequency tunability of Ba0.8Sr0.2TiO3ceramics

The effect of Mg loading on the high-frequency tunable properties and dielectric loss of Ba 0.8 Sr 0.2 Ti 1− x Mg x O 3 (BSTM) ceramics was investigated. Variation in the lattice parameters and the 90° domain configuration with Mg loading indicated a decrease in the tetragonal distortion. Additionally, the 90° domain size decreased slightly with a low Mg loading, up to 0.1 mol %, resulting in a higher domain-wall density compared with the non-doped specimen. The 0.075 mol % Mg-loaded BSTM ceramic exhibited the highest tunability; this was attributed to the domain-size effect. The loss tangent (tan δ) roughly decreased with Mg loading, due to loaded oxygen vacancies. The maximum figure of merit value (FOM = tunability/tan δ) at 10 MHz was achieved for the 0.075 mol % Mg specimen, twice that of the non-doped specimen, due to an increase in the tunability and a decrease in the loss tangent with Mg loading.