A durable-flame retardant based on tetrakis (hydroxymethyl ) phosphonium hydroxide (THPOH), urea, and trimethylolmelamine has been developed and applied to cotton fabric. The process is accomplished by padding fabric through a water solution of the three components to a wet pickup of about 75%, drying at moderate temperature, and curing at an elevated temperature. Solutions of 25-34% total solids containing the three components in a molar ratio of 2 : 4 : 1 (THPOH: urea : methylolmelamine), when applied to cotton fabrics of 8-9-oz weight, imparted flame resistance, and only minimal losses in breaking and tearing strength. The treated fabrics retained 91-95% break strength and 73-80% tear strength. Wrinkle recovery angles (W + F) of treated fabrics ranged from 280° to 306°. Wash- wear and durable-press properties are discussed. Little or no yellowing of treated fab rics was observed when bleached with sodium hypochlorite solution and scorched between heated plates. Resin add-ons of fabrics treated in this manner ranged from 15 to 19%. Flame resistance of fabrics treated by this process is retained after boiling the treated fabrics in a soap-sodium carbonate solution for 3 hr or after 15 laundering cycles.
No takes yet. Share an insight, caveat, or question.
Beninate et al. (1968) studied this question.
Synapse has enriched one closely related paper. Consider it for comparative context: