The temperature dependence of heavy-ion damage in iron: A microstructural transition at elevated temperatures

A transition is reported in the dislocation microstructure of pure Fe produced by heavy-ion irradiation of thin foils, which took place between irradiation temperatures (T irr) of 300°C and 500°C. At T irr ≤ 400°C, the microstructure was dominated by round or irregular non-edge dislocation loops of interstitial nature and with Burgers vectors b = ½ ⟨111⟩, although interstitial ⟨100⟩ loops were also present; at 500°C only rectilinear pure-edge ⟨100⟩ loops occurred. At intermediate temperatures there was a gradual transition between the two types of microstructure. At temperatures just below 500°C, mobile ½⟨111⟩ loops were seen to be subsumed by sessile ⟨100⟩ loops. A possible explanation of these observations is given.