Structural characterization of nanocrystalline hydroxyapatite and adhesion of pre-osteoblast cells

Nanocrystalline hydroxyapatite (Nano HA), a prototype of minerals of bones and teeth, attracts increasing interest in medicine and dentistry. Different parameters for synthesis and post-treatment were investigated to determine their effects on crystallinity of nano HA, and in vitro cell responses to nano HA were studied. XRD and TEM analyses indicate that the crystallinity of nano HA synthesized by a chemical method was within the range of 15–50 nm, which is adapted to natural minerals of hard tissues. Increasing the ageing temperature significantly increased the crystallinity of nano HA, while lengthening the ageing time or varying the post-ageing drying process did not have any influence on its crystallinity. Nano HA annealed between 300 and 900 °C showed a small increase in crystallinity with increasing annealing temperature due to the long-range ordering effect. Cell attachment and spreading on nano HA were lower than those on pure titanium, and decreased as the crystallinity of nano HA increased. However, cells on nano HA demonstrated well-developed filopodia and lamelliopodia, which facilitate migration of the cells on it. This may benefit osteogenesis at the interface between bone and nano HA in vivo .