The effect of 401K neutron irradiation in pure austenitic Fe 64 Cr 16 Ni 20 and Fe 59 Cr 16 Ni 25 alloys and in silicon-or titanium-doped Fe 59 Cr 16 Ni 25 was investigated by electrical-resistivity measurements. The resistivity variations were found to be consistent with irradiation-enhanced local ordering. Pure exponential kinetics were followed in the last part of the approach to equilibrium. The saturation values of the electrical resistivity, together with results obtained during annealing of unirradiated or low-temperature irradiated samples, were used to obtain the temperature dependence of the contribution of local order to the residual electrical resistivity over the temperature range 400K to 870K.