Effect of Mn substitution on crystal structure and magnetic properties of Bi1−xPrxFeO3 multiferroics

Mn substitution-driven structural and magnetic phase evolution in the predominantly antiferromagnetic polar rhombohedral (space group R3c) and weak ferromagnetic antipolar orthorhombic (space group Pnam) phases of the Bi1−x Pr x FeO3 perovskites was studied by x-ray diffraction, 57Fe Mössbauer spectroscopy and magnetometry techniques at room temperature. Mn doping was found to effectively modify both the initial structures to stabilize a new phase demonstrating incommensurable modulation. Magnetic behaviour of the Mn-containing samples changes in correlation with the evolution of their structural state. Within the compositional range of the rhombohedrally distorted compounds, the manganese substitution gives rise to suppression of the dominant antiferromagnetic interaction. In the weak ferromagnetic doping-induced phase, a gradual decrease in room temperature spontaneous magnetization takes place with increasing Mn content.