Jute fabric-reinforced poly(caprolactone) biocomposites (30–70% jute) were fabricated by compression molding. Tensile strength, tensile modulus, bending strength, bending modulus and impact strength of the non-irradiated composites (50% jute) were found to be 65 MPa, 0.75 GPa, 75 MPa, 4.2 GPa and 6.8 kJ/m2, respectively. The composites were irradiated with gamma radiation at different doses (50–1000 krad) at a dose rate of 232 krad/hr and mechanical properties were investigated. The irradiated composites containing 50% jute showed improved physico-mechanical properties. The degradation properties of the composites were observed. The morphology was evaluated by scanning electron microscope.