Synthesis of well‐defined macromonomers and comb copolymers from polymers made by atom transfer radical polymerization

Poly(n‐butyl acrylate) macromonomers with predetermined molecular weights (1300 < number‐average molecular weight < 23,000) and low polydispersity indices (<1.2) were synthesized from bromine‐terminated atom transfer radical polymerization polymers via end‐group substitution with acrylic acid and methacrylic acid. These macromonomers, having a high degree of end‐group functionalization (>90%), were radically homopolymerized to obtain comb polymers. A high macromonomer concentration, combined with a low radical flux, was needed to obtain a high conversion of the macromonomers and a reasonable degree of polymerization. By the traditional radical copolymerization of the hydrophobic macromonomers with the hydrophilic monomer N,N‐dimethylaminoethyl methacrylate (DMAEMA), amphiphilic comb copolymers were obtained. The conversions of the macromonomers and comonomer were almost quantitative under optimized reaction conditions. The molecular weights were high (number‐average molecular weight ≈70,000), and the molecular weight distribution was broad (polydispersity index ≈ 3.5). Kinetic measurements showed simultaneous decreases in the macromonomer and DMAEMA concentrations, indicating a relatively homogeneous composition of the comb copolymers over the whole molecular weight range. This was supported by preparative size exclusion chromatography. The copolymerization of poly(n‐butyl acrylate) macromonomers with other hydrophilic monomers such as acrylic acid or N,N‐dimethylacrylamide gave comb copolymers with multimodal molecular weight distributions in size exclusion chromatography and extremely high apparent molecular weights. Dynamic light scattering showed a heterogeneous composition consisting of small (6–9 nm) and large (23–143 nm) particles, probably micelles or other type of aggregates.