Modified low molecular weight polyacrylic acid as a dispersant for spontaneous coagulation casting of alumina ceramics

This is the authors' abstract. We don't add key points for this paper.

Slurries with high solid loading and low apparent viscosity are critical for spontaneous coagulation casting (SCC) and other in–situ slurry solidification techniques. This work evaluates polyacrylic acid (PA) with a low molecular weight modified as a superior dispersant (M–PA) to enhance the versatility and applicability of SCC, which traditionally employed Isobam 600AF as a dispersant in combination with Isobam 104. Varying the ratio of M–PA and Isobam 104 enabled an increase in the solid loading of alumina slurry—formulated with a commercial powder (D50=0.45 μm)—from 56 vol% to 58 vol%. The relative density of the alumina green body increased from 62.0% to 67.0%. The ceramics derived from a 56 vol% solid loading slurry, when sintered at 1550 °C, exhibited a relative density of 98.7%, Vickers hardness of 17.3 GPa, and flexural strength of 583 MPa, surpassing those of ceramics prepared using other dispersants. While the ceramics derived from a 58 vol% solid loading slurry, when sintered at 1500°C, exhibited a relative density of 98.9%, and Vickers hardness of 17.8 GPa. These findings demonstrate the potential of M–PA to broaden the applicability of SCC and suggest that the strategy of using low–molecular–weight dispersant may enable the fabrication of high–density green bodies through SCC and then high mechanical properties of ceramics under low sintering temperature.