An experimental study of the sulphide capacities in the system AlO-CaO-SiO

Measurements of the sulphide capacities in the Al2O3-CaO-SiO2 system were carried out at 1773, 1873, 1848 and 1923 K using a gas-slag equilibration technique. The experimental results along with the literature data were employed to optimize the parameters of the sulphide capacity model developed at the Division of Theoretical Metallurgy. A complete description of the Cs in the Al2O3-CaO-SiO2 system was obtained. The calculated results were found to be in good agreement with the experimental data. Comparisons of the experimental Cs values with the calculated results using the optical basicity approaches were also made. On a exécuté des mesures de capacité de sulfare, à 1773, 1873, 1848 et 1923 K du système Al2O3-CaO-SiO2, en utilisant une technique d'équilibration de gaz-laitier. On a utilisé les résultats expérimentaux ainsi que les données de la littérature pour optimiser les paramètres du modèle de capacité de sulfure développé à la Division de Métallurgie Théoretique. On a obtenu une description complète du Cs du système Al2O3-CaO-SiO2. On a trouvé que les résultats calculés étaient en accord avec les données expérimentales. On a aussi fait des comparaisons entre les valeurs expérimentales de Cs et les résultats calculés en utilisant des approches de basicité optique.