Facile Synthesis of Poly(3,4-ethylenedioxythiophene) Film via Solid-State Polymerization as High-Performance Pt-Free Counter Electrodes for Plastic Dye-Sensitized Solar Cells

A high-performance Pt-free counter electrode (CE) based on poly(3,4-ethylenedioxythiophene) (PEDOT) film for plastic dye-sensitized solar cells (DSCs) has been developed via a facile solid-state polymerization (SSP) approach. The polymerization was simply initiated by sintering the monomer, 2,5-dibromo-3,4-ethylenedioxythiophene (DBEDOT), at the temperature of 80 °C, which can be applied on the plastic substrate. The cyclic voltammetry measurements revealed that the catalytic activity of the SSP-PEDOT CE for triiodide reduction is comparable with that of the Pt CE. Under optimized conditions, the power conversion efficiency of a DSC with a N719-sensitized TiO2 photoanode and the SSP-PEDOT CE is 7.04% measured under standard 1 sun illumination (100 mW cm(-2), AM 1.5), which is very close to that of the device fabricated under the same conditions with a conventional thermally deposited Pt CE (7.35%). Furthermore, taking advantage of the compatibility of the SSP-PEDOT with the plastic substrates, a full plastic N719-sensitized TiO2 solar cell was demonstrated, and an efficiency of 4.65% was achieved, which is comparable with the performance of a plastic DSC with a sputter-deposited Pt CE (5.38%). These results demonstrated that solid-state polymerization initiated at low temperature is a facile and low-cost method of fabricating the high-performance Pt-free CEs for plastic DSCs.