One-Step Synthesis of Cross-Linked Block Polymer Precursor to a Nanoporous Thermoset

Using a simultaneous block polymerization/in situ cross-linking from a heterofunctional initiator approach, we produced a nanostructured and cross-linked block polymer in a single step from a ternary mixture of monomers and used it as a precursor for a cross-linked nanoporous material. Using 2-(benzylsulfanylthiocarbonylsulfanyl)ethanol as a heterofunctional initiator, simultaneous ring-opening transesterification polymerization of d, l -lactide in the presence of tin 2-ethylhexanoate as a catalyst and reversible addition–fragmentation chain transfer polymerization of styrene at 120 °C produced a polylactide- b -polystyrene (PLA- b -PS) block polymer. Incorporation of divinylbenzene in the polymerization mixture allowed in situ cross-linking during the simultaneous block polymerization to result in the cross-linked block polymer precursor in one step. This material was converted into cross-linked nanoporous polymer by etching PLA in a basic solution.