Control of Bubble Size and Location in Nano‐/Microscale Cellular Poly(propylene)/Rubber Blend Foams

Plastic foam with nano‐/micro‐scale cellular structures was prepared from a poly(propylene) (PP)/propylene‐ethylene copolymer (PER) blend by controlling bubble nucleation sites and bubble growth in disperse PER domains. Batch foaming experiments using a CO2 pressure quench method were conducted at room temperature. The bubble size and location were highly controlled in disperse PER domains by exploiting the differences in CO2 solubility and viscoelasticity between the PER domains and the PP matrix. The average cell diameter of PP/PER blend foams can be controlled within 0.5–2 µm by the PP/PER ratio, depressurization rate, and foaming temperature. magnified image