Synthesis and properties of Rb 2 GeF 6 :Mn 4+ red-emitting phosphors

Rb 2 GeF 6 :Mn 4+ red-emitting phosphors were synthesized by coprecipitation and their structural and optical properties were investigated by laser microscopy observation, X-ray diffraction (XRD) analysis, photoluminescence (PL) analysis, PL excitation (PLE) spectroscopy, and PL decay measurement. Single-crystalline ingots in the form of a hexagonal pyramid were prepared with a basal plane diameter of ∼2 mm. The XRD analysis suggested that Rb 2 GeF 6 crystallizes in the hexagonal structure ( ) with a = 0.5955 nm and c = 0.9672 nm. The phosphor exhibited the strong Mn 4+ -related zero-phonon line (ZPL) emission peak typically observed in host crystals with piezoelectrically active lattices such as a hexagonal lattice. The quantum efficiencies of the bulk ingot and powdered samples were 87 and 74%, respectively, with nearly the same luminescence decay time of ∼6 ms. The exact ZPL energies and related crystal-field and Racah parameters were obtained from the PL and PLE spectra by Franck–Condon analysis. Temperature-dependent PL intensities were analyzed from T = 20 to 500 K using a thermal quenching model by considering Bose–Einstein phonon statistics. A comparative discussion on the phosphor properties of Rb 2 GeF 6 :Mn 4+ and Rb 2 MF 6 :Mn 4+ with M = Si and Ti was also given.