Preparation and Performances of Castable HTPB/CL‐20 Booster Explosives

HTPB/CL‐20 castable booster explosives were prepared successfully by a cast‐cured process. Scanning electron microscope (SEM) and the charge density test were employed to characterize the molding effect of HTPB/CL‐20 explosives. The propagation reliability, detonation velocity, mechanical sensitivity, thermal decomposition characteristics and thermal stability of the HTPB/CL‐20 explosives were also measured and analyzed. The results show that, when CL‐20 content is less than 91 wt.‐%, the charges with better molding effect were obtained easily. The critical diameter of HTPB/CL‐20 explosives is less than 1 mm, which exhibits good propagation reliability. When the density of HTPB/CL‐20 charge with 91 wt.‐% CL‐20 is 1.73 g cm−3, its detonation velocity can reach 8273 m s−1. Moreover, this kind of explosives has low mechanical sensitivity and good thermal stability.