On the internal structure of Guinier-Preston zones in Al-3 at.% Ag

High-angle annular dark-field scanning transmission electron microscopy has been employed to study partially decomposed Al-3 at.% Ag. After solutionizing at 550°C and quenching to room temperature, samples of an Al-3 at.% Ag single crystal were aged for short times at 105, 140 and 180°C. Independent of the ageing temperature for these early stages, Guinier-Preston zones with a diameter of about 3 nm are found. Most of these zones consist of a silver-depleted core surrounded by a silver-rich shell. The shell structure is not uniformly pronounced. Irregularly shaped Guinier-Preston zones are common, but the shell structure dominates. No indication of different structures of the Guinier-Preston zones in Al-3 at.% Ag was found after short ageing at the three different temperatures. The shell model for Guinier-Preston zones in aluminium-rich Al-Ag alloys, which was previously proposed on the basis of X-ray and neutron scattering experiments, is thus appropriate to describe the structure of the Guinier-Preston zones in the early stages of the decomposition.