Influence of Carbon on Mechanical Properties of Cu bearing Extra Low Carbon Steel Sheets

This paper examines the effect of carbon (C) on solid solution strengthening, bake hardening and anti‐strain aging property for copper (Cu) bearing extra low carbon (ELC) steel sheets. For this purpose, five ELC steels that contain different content of C were selected. We have investigated the effect of C on mechanical properties and microstructures for the continuous annealed ELC steel sheets. Mechanical properties and microstructures were analyzed as well using uni‐axial tensile test and electron back‐scattered diffraction (EBSD) technique following pilot rolling and continuous annealing. It has been found that the addition of C increases the solid solution strengthening as well as 19.9MPa per 0.0010wt%C in yield strength. What is more, the addition of C increases the bake hardenability (BH) as well as 18.7MPa per 0.0010wt%C. In addition, the addition of C delays the recrystallization during continuous annealing process. From an industrial standpoint, it is possible to control both a stable anti‐strain aging property and high bake hardenability for the ELC steel sheets without Ti and Nb addition.