Thermally stable Ge/Ag/Ni Ohmic contact for InAlAs/InGaAs/InP HEMTs

Excellent annealed ohmic contacts based on Ge/Ag/Ni metallization have been realized in a temperature range between 385 and 500/spl deg/C, with a minimum contact resistance of 0.06 /spl Omega//spl middot/mm and a specific contact resistivity of 2.62 ×10/sup -7/ /spl Omega//spl middot/cm2obtained at an annealing temperature of 425/spl deg/C for 60 s in a rapid thermal annealing (RTA) system. Thermal storage tests at temperatures of 215 and 250/spl deg/C in a nitrogen ambient showed that the Ge/Ag/Ni based ohmic contacts with an overlay of Ti/Pt/Au had far superior thermal stabilities than the conventional annealed AuGe/Ni ohmic contacts for InAlAs/InGaAs high electron mobility transistors (HEMTs). During the storage test at 215/spl deg/C, the ohmic contacts showed no degradation after 200 h. At 250/spl deg/C, the contact resistance value of the Ge/Ag/Ni ohmic contact increased only to a value of 0.1 /spl Omega//spl middot/mm over a 250-h period. Depletion-mode HEMTs (D-HEMTs) with a gate length of 0.2 μm fabricated using Ge/Ag/Ni ohmic contacts with an overlay of Ti/Pt/Au demonstrated excellent dc and RF characteristics.