Formation and structure of nanocrystals in an Al86Ni11Yb3 alloy

The formation and structure of the nanocrystalline phase in the Al 86 Ni 11 Yb 3 alloy are investigated using differential scanning calorimetry (DSC), transmission electron and high-resolution electron microscopy, and x-ray diffraction. The nanocrystalline phase is formed upon controlled crystallization of the amorphous alloy prepared by quenching of the melt on a rapidly moving substrate. It is revealed that the nanocrystalline alloy consists of aluminum nanocrystals (5–12 nm in size) randomly distributed in the amorphous matrix. The maximum fraction of the nanocrystalline phase does not exceed 25%. The nanocrystal size substantially increases at the initial stage of isothermal treatment (at 473 K) and then changes insignificantly. It is found that nanocrystals are usually free of defects. However, some nanocrystals have a more complex microstructure with twins and dislocations. The size distributions of nanocrystals are determined at several durations of isothermal treatment. It is demonstrated that the nucleation of nanocrystals predominantly occurs through the heterogeneous mechanism. The experimental distributions are compared with those obtained from a computer simulation. The activation energy of crystallization, the time-lag, and the coefficient of ytterbium diffusion in the alloy are estimated