An experimental study was conducted on a drug delivery system (DDS), using porous apatite ceramics (PAC): hydroxyapatite block (HAb) [Ca10(PO4)6(OH)2] having a porosity of 35-48% and pore size range of 50-300 microm, and beta-tricalcium phosphate block (TCP) [Ca3(PO4)2] having a porosity of 75-80% and pore size range of 100-400 microm, for sustained release of a chemotherapeutic agent. Methotrexate (MTX) was loaded in the pores of PAC blocks by centrifuging the blocks in MTX solution. Impregnation of MTX in PAC blocks (1 cm3) was confirmed by a magnetic resonance imaging (MRI) study using Gadolinium-DTPA enhancement. The MRI showed high signal intensity in the PAC, which was confirmed by dye loading into the pores. To estimate the MTX-releasing capability of the PAC, the blocks were stored in 3 mL of phosphate-buffered saline (PBS) at 37 degrees C and the PBS was replaced every 48 h. The amount of MTX released was assayed by high-performance liquid chromatography. This study showed that MTX-impregnated PAC (0.63-2.25 mg/block) released the drug in a steady manner and maintained its concentration (0.1-1.0 microg/mL) up to 12 days. This concentration is high enough to be effective against tumor cells. Chemotherapeutic agent-impregnated PAC, prepared by simple centrifugation, could be a valuable form of local chemotherapy when used as a strut graft to repair bone defects. This new DDS material could also be used as an adjuvant to extended curettage and provide a means to reduce the recurrence of tumors without risk of systemic toxicity.
No takes yet. Share an insight, caveat, or question.
Itokazu et al. (1998) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: