High electron mobility lattice-matched AlInN∕GaN field-effect transistor heterostructures

Room temperature electron mobility of 1170cm2∕Vs is obtained in an undoped, lattice-matched, Al0.82In0.18N∕GaN field-effect transistor heterostructure, while keeping a high (2.6±0.3)×1013cm−2 electron gas density intrinsic to the Al0.82In0.18N∕GaN material system. This results in a two-dimensional sheet resistance of 210Ω∕◻. The high mobility of these layers, grown by metal-organic vapor phase epitaxy on sapphire substrate, is obtained thanks to the insertion of an optimized AlN interlayer, reducing the alloy related interface roughness scattering.